Fix ALL TurboTack Adhesive Compatibility
- All usual building substrates, natural stone, lacquered wood, stainless steel, AlMgSi1, electro-lytic galvanised steel, AlCuMg1, hot dip galvanised steel, AlMg3, steel ST1403, polystyrene, polycarbonate, PVC, ABS, polyamide, PMMA, fibreglass reinforced epoxy, polyester
- Cannot be used as a glazing sealant
- Not suitable for bonding aquariums
- Can bond natural stone but should not be used as a joint sealant on them
- Porous surfaces in water-loaded applications should be primed with Primer 150
- Non-porous and smooth surfaces can be treated with Surface Activator or cleaner
- As with all sealants, preliminary adhesion and compatibility tests are recommended
- Not suitable for PE, PP, PTFE, bituminous substrates, copper, bronze, or brass
- Do not use in applications with continuous water immersion
- Avoid contact with bitumen, tar, EPDM, neoprene, butyl, or other plasticizer-releasing materials
Fix ALL TurboTack Technical InformationTEST
Measurement | Value |
---|---|
Base | SMX Hybrid Polymer |
Consistency | Stable paste |
Curing system | Moisture curing |
Skin formation* (20°C / 65% R.H.) | Ca. 5 min |
Curing speed | Ca. 3 mm / 24 h |
Hardness | 70 ± 5 Shore A |
Density | Ca. 1.48 g/ml |
Maximum allowed distortion | ± 20% |
Elasticity modulus (ISO 37) | Ca. 2.80 N/mm² |
Maximum tension (ISO 37) | Ca. 3.60 N/mm² |
Initial tack | > 200 kg/m² |
Application temperature | +5°C → +35°C |
Temperature resistance | -40°C → +90°C |
Shelf life | 12 months unopened at +5°C → +25°C |
* Skinning time and curing speed may vary depending on environmental factors such as temperature, moisture, and substrate type.